MARSHALL STABILITY AND FLOW VALUES OF BITUMINOUS MIX SPECIMEN

The specimens to be tested are kept immersed under water in a thermostatically controlled water bath maintained at 60⁰ ± 1⁰C for 30 to 40 minutes. The specimens are taken out one by one, placed in the Marshall test head and the Marshall stability value (maximum load carried in kg. before failure) and the flow value (the deformation the specimen undergoes during loading up to the maximum load in 0.01 mm units) are noted. The corrected Marshall stability value of each specimen is determined by applying the appropriate correction factor, if the average height of the specimen is not exactly 63.5 mm. The correction factors are given in Table.

Correction Factors for Stability and Flow Value

Volume of Specimen  in Cubic Centimeters	Approximate Thickness of Specimen in mm	Correction Factors
457-470	57.1	1.19
471-482	58.7	1.14
483-495	60.3	1.09
496-508	61.9	1.04
509-522	63.5	1.00
523-535	65.1	0.96
536-546	66.7	0.93
547-559	68.3	0.89
560-573	69.9	0.86

DENSITY AND VOIDS ANALYSIS OF BITUMINOUS MIX SPECIMEN

Soon after the compacted bituminous mix specimens have cooled to room temperature, and then the weight, average thickness and diameter of the specimen are noted. The specimens are also weighed in air and then in water. The bulk density value G_b of the specimen is calculated from the weight and volume. The voids analyses are made as given below:

 

Where,

            V_v = air voids in the mix, %

                        V_b = volume of bitumen

                        VMA = voids in mineral aggregates, %

                        VFB = voids filled with bitumen %

SPECIFIC GRAVITY OF COMPACTED SPECIMEN OF BITUMINOUS MIX

The specific gravity values of the different aggregates, filler and bitumen used are determined first. The theoretical specific gravity G_t of the mix is given by-

 Where,

W₁ = percent by weight of coarse aggregate

                        W₂ = percent by weight of fine aggregate

                        W₃ = percent by weight of mineral filler

                        W₄ = percent by weight of bitumen

                        G₁ = apparent specific gravity of coarse aggregate

                        G₂ = apparent specific gravity of fine aggregate

                        G₃ = apparent specific gravity of mineral filler

            G₄ = apparent specific gravity of bitumen

PREPARATION OF TEST SPECIMEN FOR MARSHALL METHOD

The coarse aggregates, fine aggregates and the filter materials should be proportioned and mixed specified gradation of mineral aggregates and bitumen binder as per IRG: 29–1968 are given in Table. The aggregates and filler are mix together in the desired proportion as per the design requirements and fulfilling the specified gradation. The required quantity of the mix is taken so as to produce a compacted bituminous mix specimen of thickness 63.5mm, approximately.

Approximately 1200g of aggregates and filler are taken and heated to a temperature of 175⁰ to 190⁰C. The compaction mould assembly and rammer are cleaned and kept pre-heated to a temperature of 100⁰C to 145⁰C. The bitumen is heated to temperature of 121⁰C to 138⁰C and the required quantity of first trial percentage of bitumen (say, 3.5% by weight of mineral aggregates) is added to the heated aggregate and thoroughly mixed using a mechanical mixer or by hand mixing with trowel. The mixing temperature for 80/100grade bitumen may be around 154⁰C and that for 60/70grade, about 160⁰C.The mix is placed in a mould and compacted by rammer, with 50 blows on either side. The compacting temperatures may be about 138⁰C for 80/100grade bitumen and 149⁰C for 60/70grade. The compacted specimen should have thickness of 63.5mm. The weight of the aggregate taken may be may be suitably altered to obtain a thickness of 63.5±3.0 mm.  At least two specimens, but preferably three or four specimens should be prepared at each trial bitumen content which may be varied at 0.5 percent increments up to about 7.5 or 8.0 percent.

 

Specified Grading of Aggregates for Bituminous Concrete

Passing Sieve size	Retained Sieve size	Weight of Aggregate (gm)
20 mm	12.5 mm	120
12.5 mm	9.5 mm	120
9.5 mm	4.75 mm	240
4.75 mm	2.36 mm	216
2.36 mm	600 micron	216
600 micron	300 micron	72
300 micron	150 micron	72
150 micron	75 micron	84
75 micron	Filler	60
Total =		1200 gm